165 um Reduced Diameter Bending Insensitive Fibre

YOFC 165 um fibre realized reduced fibre outer diameter with excellent bending performance thanks to its bending insensitive fibre design, furthermore, by reducing the outer clad’s thickness, YOFC 165um fibre’s glass part diameter is only 80 um and has the similar MFD to standard G.657.B3 fibre.

YOFC 165 um reduced diameter bending insensitive fibres delivers the outstanding bending performance to a 5 mm radius for demanding applications while maintaining compatible with conventional G.652.D and G.657 fibres. It is an excellent choice for application where small size, small bend radii may be encountered.

Applications

Small-sized optical component

Characteristics
  • Outstanding bending performance and compatible with G 652.D and G.657 fibres.
  • Proof-tested to 200 KPSI to ensure reliability.
  • 56% less CSA than conventional 250 μm coated fibre enabling smaller size optical component.

Specifications

Characteristics

Conditions

Specified values

Units

Optical Characteristics

Attenuation

1550 nm

≤ 0.30

[dB/km]

Zero Dispersion Wavelength (λ0)

--

1300 - 1324

[nm]

Zero dispersion Slope (S0)

--

≤ 0.092

[ps/(nm2·km)]

Fibre Cut-off Wavelength

--

≤ 1520

[nm]

Mode Field Diameter (MFD)

1550 nm

9.15 - 10.15

[μm]

Geometrical Characteristics

Cladding Diameter

--

80.0 ± 0.5

[μm]

Cladding Non-Circularity

--

≤ 0.7

[%]

Cladding Non-Circularity

--

155 - 175

[μm]

Coating/Cladding Concentricity Error

--

≤ 12

[μm]

Coating Non-Circularity

--

≤ 6.0

[%]

Core/Cladding Concentricity Error

--

≤ 0.3

[μm]

Curl (radius)

--

≥ 4

[m]

Delivery Length

--

≥ 0.5

[km]

Environmental Characteristics 1550 nm & 1625 nm

Temperature Dependence Induced Attenuation

-60℃ to +85℃

≤ 0.05

[dB/km]

Temperature-Humidity Cycling Induced Attenuation

-10°C to +85°C, 98% RH

≤ 0.05

[dB/km]

Watersoak Dependence Induced Attenuation

23°C, for 30 days

≤ 0.05

[dB/km]

Damp Heat Induced Attenuation

85°C and 85% RH, for 30 days

≤ 0.05

[dB/km]

Dry Heat Aging

85℃, for 30 days

≤ 0.05

[dB/km]

Mechanical Specifications

Proof Test

--

200

[KPSI]

Macro-bend Induced Loss

1 Turn Around a Mandrel of 5 mm Radius 1550 nm

≤ 0.1

[dB]

1625 nm

≤  0.3

[dB]

1 Turn Around a Mandrel of 7.5 mm Radius

1550 nm

≤ 0.08

[dB]

1625 nm

≤ 0.25

[dB]

1 Turn Around a Mandrel of 10 mm Radius 1550 nm

≤ 0.03

[dB]

1625 nm

≤ 0.1

[dB]

Dynamic Fatigue Parameter (nd)

--

≥ 20

--

Tensile Strength F15% ≥ 3.14 [GPa]
F50%

≥ 3.80

[GPa]