| Item | Typical value | Unit | |
|---|---|---|---|
|
Viscosity, 25°C |
9900 | mPa•s | |
| Density | 1.02 | g•cm-3 | |
| Refractive index | 1.476 | n/a | |
| Item | Typical value | Unit | |
|---|---|---|---|
| Elongation* | 73 | % | |
| Tensile strength* | 0.60 | MPa | |
| Modulus, 2.5% strain* | 1.50 | MPa | |
| Glass transition temperature | -24.3 | °C | |
| Refractive index | 1.490 | n/a | |
| 95% cure dose | 0.2 | J•cm-2 | |
| Curing shrinkage | 2.5 | % | |
| Thermal weight change at 200°C for 40min |
4.5 | % | |
| Adhesion to glass | 0.14 | N/cm | |
*Cured film thickness 150μm, test temperature at 23±2°C, humidity at 50±5%
LARMOR®YP-037 is a light curable material; protect this product from all sources of ultraviolet light, including fluorescent lighting and sunlight to prevent premature curing. It is recommended that this coating be stored in a dry place in unopened, undamaged, original containers at temperatures between 15° C and 30° C. Storage or shipment in cold conditions may result in a phase separation which is reversible and is corrected by heating for 24 hours at 50°C.
LARMOR®YP-037 has a recommended shelf life of 12 months from the date of manufacture, provided that the above stated storage conditions are properly maintained.
This product may cause skin and/or eye irritation and skin sensitization. Material safety data sheet for all products is also available from your Polytech sales representative. All safety and handling recommendations should be followed carefully.
LARMOR®YP-037 is manufactured using fine filtration techniques designed to eliminate fibre strength problems and ensure uniform product performance.